HV300-600 and 2B BA, 2Cr13 stainless steel Cold Rolled Strip with
2Cr13 cold rolled stainless steel strip with thickness:0.1-0.8mm
width: 10-240mm HV300-600 Surface:2B BA
2Cr13 quenching state high hardness, good corrosion resistance. For
steam turbine leaf blade.The 2Cr13 density 7.75g/m3, 2Cr13
quenching hardness is: Average the 2Cr13 quenching temperature in
980 ~ 1050 ℃, take the 980 ℃ heating oil quenching hardness is
significantly lower than 1050 ℃ heating oil quenching, 980 ℃ oil
quenching hardness of 45 to50HRC 1050 ℃ oil quenching hardness
after high 2HRC. But the the 1050 ℃ quenching organization coarse
grain brittleness. Recommends using 1000 ° C Hardening can get a
better organization and hardness. 2cr13 stainless steel 2Cr13
martensitic stainless steel, welded to preheat. And Q235 welded
austenitic stainless steel electrode without preheating, such as
are A302.A307 line. Welding to control the dilution rate of the
weld does not swing the welding, using a smaller current.
Mainly used for Steam Turbine Blades.and other kinds of blades.
Thickness:0.1-0.8mm (tolerance:±0.005mm).Also we could satisfactory
to you according to your special requirements.
Width: Usually 10-240mm, Tolerance: (±0.01mm). Also we could
satisfactory to you according to your special requirements.
Vicker Hardness: HV300-600. HB192-223
≥635(after the quenching and tempering treatment )
Stainless steel theoretical weight formula:
Weight (kg) = thickness (mm) × width (mm) x length (mm) × density
Stainless steel gravity:
Chromium stainless take 7.75 ton / M3
Chrome-nickel stainless steel take 7.93 ton / M3
Iron take 7.87 ton / M3
Better oxidation resistance, high hardness, good temperature
resistance, is generally used as a normal furnace or motorcycle